| Customization: | Available |
|---|---|
| Material: | Sbs/PE/APP/Py |
| Thicknesss: | 3 /4 / 5 mm |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Superior Waterproofing, Long-lasting Protection - SBS/APP Modified Bitumen Waterproof Membrane
Manufactured in compliance with GB18242-2008,
our waterproof membranes are made from high-quality bitumen from Qilu Petrochemical and modified with APP elastomer from Baling Petrochemical or APP plastomer.
Available in various types, including colored sand, slate, PE film, aluminum, composite felt, polyester felt, as well as self-adhesive membranes and green roof waterproof membranes.
Custom sizes and specifications are also available.
Excellent Performance: High-temperature stability, cold resistance, superior aging resistance
Wide Applications: Suitable for industrial and residential buildings, bridges, tunnels, grain storage, parking lots, and more
Easy Installation: Simple application, eco-friendly, lifespan of 10 to 50 years
SBS modified bitumen waterproof membrane is ideal for cold climates and high-movement structures, while APP modified bitumen waterproof membrane is best for hot climates and intense sun exposure.
Premium Quality, Reliable Protection - Contact Us for Custom Orders!
Standard: GB18242-2008
| NO. | ITEM | Parameter | |||||
| I | II | ||||||
| PY | G | PY | G | PYG | |||
| 1 | Soluble Content/(g/m²) ≥ | 3mm | 2100 | -- | |||
| 4mm | 2900 | -- | |||||
| 5mm | 3500 | ||||||
| Test Phenomenon | -- | Base is non - combustible | -- | Base is non - combustible | -- | ||
| 2 | Heat Resistance | °C | 110 | 130 | |||
| ≤mm | 2 | ||||||
| Test Phenomenon | No dripping, dropping | ||||||
| 3 | Low - temperature Flexibility/°C | -7 | -15 | ||||
| No cracks | |||||||
| 4 | Water Impermeability 30min | 0.3Mpa | 0.2Mpa | 0.3Mpa | |||
| 5 | Tensile Force | Maximum Peak Tensile Force/(N/50mm) ≥ | 500 | 350 | 800 | 500 | 900 |
| Secondary Peak Tensile Force/(N/50mm) ≥ | -- | -- | -- | -- | 800 | ||
| Test Phenomenon | During stretching, there is no asphalt cover cracking or base separation in the middle of the specimen | ||||||
| 6 | Elongation Rate | Elongation Rate at Maximum Peak/% ≥ | 25 | -- | 40 | -- | -- |
| Elongation Rate at Second Peak/% ≥ | -- | -- | 15 | ||||
){kind=link}